- 核反应堆压力容器接管安全端堆焊修复结构的LBB分析
- Leak-before-break analysis of a dissimilar metal welded overlay structure for connecting pipe-nozzle of nuclear reactor pressure vessel to safe end
- 核技术 2014年37卷第1期文章编号：010603
- 作者机构：
  
  华东理工大学承压系统与安全教育部重点实验室,上海,200237
- 作者简介：
  
  [ "通讯作者: 王国珍，E-mail: gzwang@ecust.edu.cn E-mail:gzwang@ecust.edu.cn" ]
- 基金信息：
  
  国家自然科学基金项目(51075149)、国家863项目(2012AA040103)及中央高校基本科研业务费专项资金资助()
- DOI：10.11889/j.0253-3219.2014.hjs.37.010603
  中图分类号：
- 纸质出版日期：2014-01-20
- 稿件说明：
移动端阅览
魏敏, 王国珍, 轩福贞, 等. 核反应堆压力容器接管安全端堆焊修复结构的LBB分析[J]. 核技术, 2014,37(1):010603

WEI Min, WANG Guozhen, XUAN Fuzhen, et al. Leak-before-break analysis of a dissimilar metal welded overlay structure for connecting pipe-nozzle of nuclear reactor pressure vessel to safe end[J]. Nuclear techniques, 2014, 37(1): 010603
魏敏, 王国珍, 轩福贞, 等. 核反应堆压力容器接管安全端堆焊修复结构的LBB分析[J]. 核技术, 2014,37(1):010603 DOI： 10.11889/j.0253-3219.2014.hjs.37.010603.

WEI Min, WANG Guozhen, XUAN Fuzhen, et al. Leak-before-break analysis of a dissimilar metal welded overlay structure for connecting pipe-nozzle of nuclear reactor pressure vessel to safe end[J]. Nuclear techniques, 2014, 37(1): 010603 DOI： 10.11889/j.0253-3219.2014.hjs.37.010603.

摘要

核反应堆压力容器接管安全端异种金属焊接接头在服役中通常会产生高温高压水环境中的应力腐蚀裂纹扩展。目前减轻和修复这种裂纹的技术是在安全端管接头外表面堆焊一层更抗腐蚀的镍基合金(Alloy52M)材料。本文通过三维结构的有限元断裂力学分析，计算得到了堆焊修复结构的“先漏后断” (Leak-before-break

LBB)曲线和韧带失稳线，并分析了堆焊层厚度对LBB安全边际的影响。结果表明，堆焊修复后结构的LBB曲线和韧带失稳线在没有堆焊层结构的曲线上方，且随堆焊层厚度的增加，LBB曲线和韧带失稳线上移，表明堆焊修复及堆焊层厚度的增加使安全端结构的LBB安全边际增大。

Abstract

Background: Primary water stress corrosion cracking (PWSCC) is commonly produced in the dissimilar metal welded joints for connecting the pipe-nozzles of nuclear reactor pressure vessels to the safe ends. The technology to repair and mitigate PWSCC is usually to make the weld overlay of higher corrosion resistant Alloy52M on the pipe joints. Purpose: We need to assess the integrity of the welded overlay structures

and to make Leak-before-break (LBB) analyses. The effect of the weld overlay thickness on the LBB behavior needs to be studied. Methods: Based on the three-dimensional finite element fracture mechanics analyses

the ABAQUS software was applied to construct the LBB curves and ligament instability lines of the dissimilar metal welded overlay structures. The effects of the weld overlay thickness on the LBB curves and ligament instability lines were analyzed. Results: The results show that the LBB curves and ligament instability lines with the weld overlay are located above those without the weld overlay. With increasing weld overlay thickness

the LBB curves and ligament instability lines both shift upward. Conclusion: The weld overlay can increase the LBB safe margin of the dissimilar metal welded joints. With increasing weld overlay thickness

the LBB safe margin of the joint structure can be further increased.Cited