D2钢电子束表面改性抗微动磨损性能研究

吴爱民; 刘捍卫; 邹建新; 周仲荣; 董闯

doi:null

您当前的位置：

首页 >

文章列表页 >

D2钢电子束表面改性抗微动磨损性能研究

更新时间：2021-03-12

- D2钢电子束表面改性抗微动磨损性能研究
- High current pulsed electron beam modification on fretting wear behavior of D2 die steel
- 核技术 2002年第9期
- 作者机构：
  
  1. 大连理工大学三束材料改性国家重点实验室
  2. 西南交通大学摩擦学研究所
  3. 大连理工大学三束材料改性国家重点实验室大连理工大学材料工程系大连,116024
  4. ,成都,610031
- 作者简介：
- 基金信息：
- DOI：
  中图分类号： TG174.4
- 纸质出版日期：2002-09-01
- 稿件说明：
移动端阅览
[1]吴爱民,刘捍卫,邹建新,周仲荣,董闯.D2钢电子束表面改性抗微动磨损性能研究[J].核技术,2002(09):758-765.

WU Aimin 1 LIU Hanwei 2 ZOU Jianxin 1 ZHOU Zhongrong 2 DONG Chuang 1 1. High current pulsed electron beam modification on fretting wear behavior of D2 die steel[J]. Nuclear techniques, 2002, (9): 758-765.
[1]吴爱民,刘捍卫,邹建新,周仲荣,董闯.D2钢电子束表面改性抗微动磨损性能研究[J].核技术,2002(09):758-765. DOI：

WU Aimin 1 LIU Hanwei 2 ZOU Jianxin 1 ZHOU Zhongrong 2 DONG Chuang 1 1. High current pulsed electron beam modification on fretting wear behavior of D2 die steel[J]. Nuclear techniques, 2002, (9): 758-765. DOI：

摘要

利用强流脉冲电子束（HCPEB）技术对D2钢进行了表面改性处理。结果表明

电子束轰击试样近表层组织结构发生了很大变化

且亚表层显微硬度明显增加。微动磨损结果显示

电子束处理可以改善D2钢抗微动磨损性能

预涂覆TiN和Cr层效果更明显。磨痕SEM分析表明

涂覆Cr层的样品微动磨损主要机制是粘着和氧化

而TiN涂层及电子束直接处理试样主要磨损机制则是表面疲劳微裂纹的扩展和断裂产生的剥落颗粒

在摩擦面造成磨粒磨损

同时也伴随轻微的粘着和氧化

其磨损机制相对比较复杂

Abstract

This paper studied the effect of high current pulsed electron beam (HCPEB) treatment on fretting wear ability of D2 die steel. It is shown that the most pronounced structural changes occur in the near-surface region

where the energy deposition is at its maximum. The fretting tests under dry condition were carried out on both treated and untreated specimens. The HCPEB treatment increases the fretting wear resistance significantly

and the improvement is further enhanced by surface pre-alloying by TiN and Cr. SEM analysis of the wear scars showed that the fretting wear mechanism of Cr coating is adhesive and oxidation wear

that of the TiN coating and non-coating D2 die steel is particle detachment through the propagation and fracture of fatigue microcracks on surface

and slight adhesive and oxidation wear is found

its wear mechanism is more complex.

关键词

Keywords

references

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

模具钢电子束表面改性研究

腐蚀对微结构金属试样表面沸腾换热特性的影响研究

靶流对磁控溅射CrN金属双极板耐腐蚀性能的影响

电子束表面改性对变形镁合金AZ31结构和性能的影响

强流脉冲电子束处理对过共晶铝硅合金Al-25Si微观组织和耐蚀性的影响