He<sup>+</sup>注入Si（100）缺陷退火效应的慢正电子束研究

张天昊; 翁惠民; 范扬眉; 杜江峰; 周先意; 韩荣典; 张苗; 林成鲁

doi:null

您当前的位置：

首页 >

文章列表页 >

He⁺注入Si（100）缺陷退火效应的慢正电子束研究

更新时间：2021-03-12

- He⁺注入Si（100）缺陷退火效应的慢正电子束研究
- Exploring of defects in He~+ implanted Si(100) by slow positron beam
- 核技术 2001年第4期
- 作者机构：
  
  1. 中国科学技术大学近代物理系,合肥,230027
  2. 中国科学院上海冶金研究所!上
- 作者简介：
- 基金信息：
  
  (No.ZX069);(No.ZX069)
- DOI：
  中图分类号： TN305
- 纸质出版日期：2001-04-01
- 稿件说明：
移动端阅览
[1]张天昊,翁惠民,范扬眉,杜江峰,周先意,韩荣典,张苗,林成鲁.He~+注入Si(100)缺陷退火效应的慢正电子束研究[J].核技术,2001(04):253-258.

ZHANG Tianhao WENG Huimin FAN Yangmei DU Jiangfeng ZHOU Xianyi HAN Rongdian. Exploring of defects in He~+ implanted Si(100) by slow positron beam[J]. Nuclear techniques, 2001, (4): 253-258.
[1]张天昊,翁惠民,范扬眉,杜江峰,周先意,韩荣典,张苗,林成鲁.He~+注入Si(100)缺陷退火效应的慢正电子束研究[J].核技术,2001(04):253-258. DOI：

ZHANG Tianhao WENG Huimin FAN Yangmei DU Jiangfeng ZHOU Xianyi HAN Rongdian. Exploring of defects in He~+ implanted Si(100) by slow positron beam[J]. Nuclear techniques, 2001, (4): 253-258. DOI：

摘要

用慢正电子束探针测量了经剂量为 5× 10 16cm-2 的 140keVHe+ 注入的Si（10 0 ）单晶S参数与正电子入射能量的关系

得到了注入产生缺陷的分布规律

发现近表面区域损伤不大

缺陷主要是直径小于 1nm的空位或空位团

较深的射程末端区域损伤严重

缺陷主要是微空洞和微气泡。对退火效应的研究表明

低温下退火空位缺陷得到了很好的消除

而高温下退火微空洞和微气泡发生融合

而且尺度增加

Abstract

Si(100) crystal implanted by 5×10 16 cm -2

140keV He + was probed by slow positron beam

and defect distribution along depth was obtained from the relation between S parameter and positron incidence energy. The near surface region of implanted sample was only slightly damaged. Small vacancies and vacancy clusters less than 1nm in diameter were the dominant defects

while the deeper region around the He + projected range was heavily damaged and had dense larger helium microbubbles and microvoids. Thermal anneal study at different temperatures showed that low temperature annealing could remove most vacancy-type defects effectively. However

annealing at high temperature enlarged the diameters of microbubbles and microvoids.

关键词

Keywords

references

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

燃料元件基体石墨Xe离子辐照缺陷的慢正电子束研究

Al₂O₃/ZrO₂纳米复合陶瓷的微结构及缺陷的正电子寿命研究

Cr和Mo对Fe₃Al合金中微观缺陷和电子密度的影响

高温超导外延薄膜YBα₂Cu₃O_7-x中空位型缺陷的低能正电子寿命研究

裂变快中子辐照在GaAs中产生缺陷的正电子湮没研究

He+注入Si（100）缺陷退火效应的慢正电子束研究

Exploring of defects in He~+ implanted Si(100) by slow positron beam

DOI：

摘要

Abstract

关键词

Keywords

references

He⁺注入Si（100）缺陷退火效应的慢正电子束研究