Defect study of electrodeposited nanocrystalline Ni by positronannihilation technique

WU Qiuyun CHU Yelong XIONG Liangyue SUN Xiukui HU Zhuangqi

您当前的位置：

首页 >

文章列表页 >

Defect study of electrodeposited nanocrystalline Ni by positronannihilation technique

更新时间：2021-04-09

- Defect study of electrodeposited nanocrystalline Ni by positronannihilation technique
- NUCLEAR TECHNIQUES Issue 4, (1998)
- 作者机构：
  
  1. 中国科学院金属研究所
  2. 辽宁省材料与氢重点实验室
  3. 中国科学院金属研究所辽宁省材料与氢重点实验室
- 作者简介：
- 基金信息：
- DOI：
  CLC： TL34
- Published：01 April 1998
- 稿件说明：
移动端阅览
[1]吴秋允,初业隆,熊良铖,孙秀魁,胡壮麒.电镀纳米镍缺陷的正电子研究[J].核技术,1998(04):213-216.

WU Qiuyun CHU Yelong XIONG Liangyue SUN Xiukui HU Zhuangqi. Defect study of electrodeposited nanocrystalline Ni by positronannihilation technique[J]. Nuclear techniques, 1998, (4).
[1]吴秋允,初业隆,熊良铖,孙秀魁,胡壮麒.电镀纳米镍缺陷的正电子研究[J].核技术,1998(04):213-216. DOI：

WU Qiuyun CHU Yelong XIONG Liangyue SUN Xiukui HU Zhuangqi. Defect study of electrodeposited nanocrystalline Ni by positronannihilation technique[J]. Nuclear techniques, 1998, (4). DOI：

摘要

用正电子寿命谱研究了电镀纳米镍（～２０ｍｍ）中的微观缺陷，分析了缺陷中的氢对正电子寿命的影响。实验结果表明：界面存在单空位大小的自由体积、６－１０个空位大小的自由体积和微孔洞三类缺陷；纳米镍在５００℃真空退火２ｈ后，中间寿命和最长寿命的强度不受影响，表明中间寿命和最长寿命所对应的缺陷具有很好的热稳定性。

Abstract

Defects in electrodeposited nanocrystalline Ni and the effect of hydrogen on the positron lifetime have been studied by the positron annihilation technique. There exist three kinds of defects at the interface

i. e. the free volumes with a monovacancy

a cluster of 6-10 vacancies and a micro-void

respectively. It is found that the moderate and longest lifetimes will not be affected when the nano-Ni is annealed at 500℃ in vacuum for 2h

which suggests that the defects related to these lifetimes show surprisingly great thermal stability.

关键词

Keywords

references

Views

105

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Application of positron annihilation to study the effect of calcium oxide addition on the sintering process of alumina nanoceramics

Positron annihilation study on defect repair of pure iron and RPV steel under electropulsing treatment

Study on the microstructure and defects of Al₂O₃/ZrO₂ nano-composites by positron lifetime spectroscopy

Microstructures of the phase transition of nano-magnesium hydroxide to nano-magnesium oxide by positron annihilation lifetime spectroscopy

Positron annihilation spectroscopy characterize PDMS-MIL-101 hybridmembrane

Related Author

YANG Xuanye

ZHAO Wenzheng

ZHANG Simin

WEN Haiyi

WU Yichu

WEN Haiyi

YANG Xuanye

ZHAO Wenzeng

Related Institution

School of Physics and Technology, Hubei Key Laboratory of Nuclear Solid State Physics, Wuhan University

Suzhou Nuclear Power Research Institute

School of Physics and Technology, Hubei Key Laboratory of Nuclear Solid State Physics, Wuhan University

School of Physics and Technology, National Demonstration Center for Experimental Physics Education(Wuhan University), Hubei Nuclear Solid Physics Key Laboratory, Wuhan University

东华理工大学

AI问答

Address：2019 Jialuo Road, Jiading, Shanghai, China Postal code：201800
Tel：021-39194977 Email：LHB@sinap.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 沪ICP备05005479号-1 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.
Total Visits：880840 Visits Today：367

⁰