Corrosion of Arion beam irradiated Al and Al-Mg coatings in aqueous solution

更新时间：2021-04-09

- Corrosion of Arion beam irradiated Al and Al-Mg coatings in aqueous solution
- NUCLEAR TECHNIQUES Issue 7, (1995)
- 作者机构：
  
  国家自然科学基金会
- 作者简介：
- 基金信息：
- DOI：
  CLC： TG174.44
- Published：01 July 1995
- 稿件说明：
移动端阅览
[1]方勤学.用离子束技术制备的铝和铝－镁镀层在水溶液中的腐蚀研究[J].核技术,1995(07):430-434.

Fang Qinxue. Corrosion of Arion beam irradiated Al and Al-Mg coatings in aqueous solution[J]. Nuclear techniques, 1995, (7).
[1]方勤学.用离子束技术制备的铝和铝－镁镀层在水溶液中的腐蚀研究[J].核技术,1995(07):430-434. DOI：

Fang Qinxue. Corrosion of Arion beam irradiated Al and Al-Mg coatings in aqueous solution[J]. Nuclear techniques, 1995, (7). DOI：

摘要

用拉力实验检验Ａｌ和Ａｌ－Ｍｇ镀层在基体金属ＥＮ８钢上的附着力；在ｐＨ＝５．６的醋酸缓蚀液中测量样品的腐蚀电位和进行浸泡实验．结果表明，镀层中的镁元素能有效地对样品进行阴极保护，提高了样品的耐腐蚀性能．

Abstract

The 120nm coatings of Al and Al-Mg on low carbon steel EN8 have been irradiated with 65keV

6×1016 Ar+2/cm2. Adhesion of the coatings on the substrate is tested. The corrosion potential measurement and immersion test are carried out in acetic acid buffer solution with pH=5.6. The experiments indicate that the corrosion resistance of the sample increases effectively due to the cathodic protection of magnesium in the coating.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Electrochemical study of ion-beam irradiated aluminium and aluminium-magnesium coating on steel surface

Mechanism of corrosion resistance for alloys prepared by surface metallurgy with Cr and Ta ion beams

Preparation of Ta-GCr15 amorphous film by ion beam mixing and its properties

Anodic polarization of hard aluminium: the influence of ion beam twice mixing on corrosion behaviour

The corrosion resistance of No.45 steel mixed with several different elements

Related Author

Fang Qinxue

Wang Peilu

Peilu Wang

Jingyun Jiang

Zhongyang Liu

Jie Weng

Peilu Wang

Zhongyang Liu

Related Institution

Heavy Ion Institute, Peking University

Institute of Nuclear Science and Technology of Sichuan University

Institute of Nuclear Science and Technology, Sichuan University

Sichuan University

Institute of Nuclear Science and Technology, Sichuan Vniversity

AI问答

Address：2019 Jialuo Road, Jiading, Shanghai, China Postal code：201800
Tel：021-39194977 Email：LHB@sinap.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 沪ICP备05005479号-1 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.
Total Visits：880780 Visits Today：307

⁰