A study of hydrogen-defects interaction in corrosion fatigue process by positron annihilation

Yu Fanhua Zheng Wanhui

您当前的位置：

首页 >

文章列表页 >

A study of hydrogen-defects interaction in corrosion fatigue process by positron annihilation

更新时间：2021-04-09

- A study of hydrogen-defects interaction in corrosion fatigue process by positron annihilation
- NUCLEAR TECHNIQUES Issue 3, (1993)
- 作者机构：
  
  1. 中国科学院上海原子核研究所
  2. 上海材料研究所,上海,201800
  3. ,上海,200433
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：01 March 1993
- 稿件说明：
移动端阅览
[1]俞方华,郑万辉,郑文龙,朱锡英,苏立民,闵国全.腐蚀疲劳断裂前氢与缺陷相互作用的正电子湮没研究[J].核技术,1993(03):134-140.

Yu Fanhua Zheng Wanhui. A study of hydrogen-defects interaction in corrosion fatigue process by positron annihilation[J]. Nuclear techniques, 1993, (3): 134-140.
[1]俞方华,郑万辉,郑文龙,朱锡英,苏立民,闵国全.腐蚀疲劳断裂前氢与缺陷相互作用的正电子湮没研究[J].核技术,1993(03):134-140. DOI：

Yu Fanhua Zheng Wanhui. A study of hydrogen-defects interaction in corrosion fatigue process by positron annihilation[J]. Nuclear techniques, 1993, (3): 134-140. DOI：

摘要

用正电子湮没谱和加热释氢研究了低合金高强钢人工海水腐蚀疲劳断裂前经若干小时疲劳的样品。实验结果表明

腐蚀疲劳早期阶段产生的位错、空位团以及钢中晶界是氢的捕获位

其捕获氢量随疲劳时间增加。氢与空位相互作用使空位团尺寸增加

数目增多

氢与位错相互作用促使位错增殖且随疲劳时间增加。晶界与氢相互作用能随疲劳时间、晶界捕获氢量增加而降低。碳化物沿晶析出促进了晶界捕获氢。较低的晶界-氢结合能有利于氢沿晶运动

促使预裂缝沿晶发展。

Abstract

Positron annihilation spectroscopy and thermal release of hydrogen have been employed to study the 40CrNiMo high strength steel in seawater corrosion fatigue process before fracture. It was found that dislocations

vacancy clusters or microvoids and grain boundaries were the trapping seats for hydrogen

the amount of hydrogen trapped by these defects increased with corrosion fatigue duration. Dislocation multiplication and the increase of number and size of vacancy clusters or microvoids due to interaction between hydrogen and defects were observed. In addition

interaction energy between hydrogen and both dislocation and grain boundary

especialy the latter

decreased with corrosion fatigue duration

which may be favourable to promote hydrogen movement and the pre- cracking fracture along grain boundaries.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Investigation of interaction between hydrogen and defects in corrosion fatigue fracture process by positron annihilation

Application of positron annihilation techniques in non-destructive testing

A study of damages in GaAs induced by 5.0MeV and 9.5MeV fastneutron irradiation using positron annihilation technique

X-ray diffraction and positron annihilation study on crystalline process of Fe_73.5Cu₁Nb₃Si_13.5B₉ amorphous alloy

A study of the influence of γ-irradiation on brittleness of amorphous alloy Fe₇₈Si₉B₁₃

Related Author

Yu Fanghua

郑文龙

苏立民

朱锡英

闵国全

项开华

ZENG Hui

CHEN Zhiqiang

Related Institution

Shanghai Institute of Nuclear Research, Academia Sinica, Shanghai 201800)Zheng Wenlong Su Limin Zhu Xiying Min Guoquan

同济大学

School of Physics and Technology, Hubei Key Laboratory of Nuclear Solid State Physics, Wuhan University

Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Jiading Campus

Center of Plant Life Management, Suzhou Nuclear Power Research Institute

AI问答

Address：2019 Jialuo Road, Jiading, Shanghai, China Postal code：201800
Tel：021-39194977 Email：LHB@sinap.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 沪ICP备05005479号-1 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.
Total Visits：880007 Visits Today：529

⁰