A Mdssbauer study of Sm20Fe70Ti10 samples melt - spun with different quenching rates

Qian Xiangrong Chen Mingxing Chen Li Jin Huijuan Chen Lijun Xu Guiqin

您当前的位置：

首页 >

文章列表页 >

A Mdssbauer study of Sm₂₀Fe₇₀Ti₁₀ samples melt - spun with different quenching rates

更新时间：2021-04-09

- A Mdssbauer study of Sm₂₀Fe₇₀Ti₁₀ samples melt - spun with different quenching rates
- NUCLEAR TECHNIQUES Issue 8, (1992)
- 作者机构：
  
  1. 上海钢铁研究所
  2. 上海钢铁研究所,上海,200940
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：01 August 1992
- 稿件说明：
移动端阅览
[1]钱祥荣,陈明星,陈利,金慧娟,陈丽君,许桂琴.快淬Sm_(20)Fe_(70)Ti_(10)永磁合金的穆斯堡尔效应研究[J].核技术,1992(08):461-464.

Qian Xiangrong Chen Mingxing Chen Li Jin Huijuan Chen Lijun Xu Guiqin. A Mdssbauer study of Sm₂₀Fe₇₀Ti₁₀ samples melt - spun with different quenching rates[J]. Nuclear techniques, 1992, (8): 461-464.
[1]钱祥荣,陈明星,陈利,金慧娟,陈丽君,许桂琴.快淬Sm_(20)Fe_(70)Ti_(10)永磁合金的穆斯堡尔效应研究[J].核技术,1992(08):461-464. DOI：

Qian Xiangrong Chen Mingxing Chen Li Jin Huijuan Chen Lijun Xu Guiqin. A Mdssbauer study of Sm₂₀Fe₇₀Ti₁₀ samples melt - spun with different quenching rates[J]. Nuclear techniques, 1992, (8): 461-464. DOI：

摘要

用熔体快淬继而进行晶化处理制备Sm

试样。内禀矫顽力随淬火速率的增加而增大

其最大值为3.2（1000/4π）kA/m。综合穆斯堡尔效应和X射线衍射的方法

发现合金是由SmFe

、SmFe

、一种特定的顺磁相和少量Sm

相所组成的。

Abstract

Sm20Fe70oTi10 samples were prepared by melt - spinning and subsequent crystallization. The intrinsic coercivity increases with the increase of quenching rate and the maximum value was 3. 2（1000/4π）kA/m. The combination of Mossbauer spectroscopy and X -ray diffaction has shown that the alloy consists of SmFe2

SmFe3

an undetermined paramagnetic phase and the minor phase of Sm2Fe17.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

SmCo₅永磁合金回火效应的正电子湮没研究

Related Author

何永枢

季国坤

石岩

金汉民

Related Institution

中国科学院高能物理研究所

吉林大学

AI问答

Address：2019 Jialuo Road, Jiading, Shanghai, China Postal code：201800
Tel：021-39194977 Email：LHB@sinap.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 沪ICP备05005479号-1 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.
Total Visits：880771 Visits Today：298

⁰