Microstructure and properties of silver films obtained using ion beam composite deposition

JIN Jie QIU Weiwei WANG Jinhui GUO Huibin

doi:null

您当前的位置：

首页 >

文章列表页 >

Microstructure and properties of silver films obtained using ion beam composite deposition

更新时间：2021-03-05

- Microstructure and properties of silver films obtained using ion beam composite deposition
- NUCLEAR TECHNIQUES Vol. 33, Issue 12, (2010)
- 作者机构：
  
  北京机械工业自动化研究所
- 作者简介：
- 基金信息：
- DOI：
  CLC： TB43
- Published：01 December 2010
- 稿件说明：
移动端阅览
[1]金杰,邱维维,王锦辉,郭会斌.IBAD和磁控溅射对银膜性能的影响[J].核技术,2010,33(12):918-922.

JIN Jie QIU Weiwei WANG Jinhui GUO Huibin. Microstructure and properties of silver films obtained using ion beam composite deposition[J]. Nuclear techniques, 2010, 33(12): 918-922.
[1]金杰,邱维维,王锦辉,郭会斌.IBAD和磁控溅射对银膜性能的影响[J].核技术,2010,33(12):918-922. DOI：

JIN Jie QIU Weiwei WANG Jinhui GUO Huibin. Microstructure and properties of silver films obtained using ion beam composite deposition[J]. Nuclear techniques, 2010, 33(12): 918-922. DOI：

摘要

本文主要研究用离子束辅助沉积（IBAD）和磁控溅射不同沉积技术在9Cr18钢材上沉积软金属银固体润滑膜。用百格刀划格法、SEM和MS-T3000多功能摩擦磨损仪等测试方法测试沉积银膜与基材间的结合力、银膜的显微结构和摩擦磨损性能等。结果表明

与磁控溅射沉积技术相比

IBAD技术制备的银膜形成一层化学冶金结合与机械啮合结合的过渡层

可提高膜层与基材的结合力

增加膜层的耐磨性。

Abstract

Using ion beam composite deposition method Magnetron sputtering deposition

soft metal solid lubricant of Ag film was grown on 9Crl8 steel substrate.The microstructures and friction properties were measured by means of the hundred cell knife scratch method

MS-T3000 multi-meter friction and wear testing and scanning electron microscopy.The results showed that compared with the magnetron sputtering method

a transition layer bonded with chemical metallurgy and mechanical engagement is formed after ion beam composite deposition.The transition layer can be attributed to the strong adhesion between the film and the substrate.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Au-Pt coatings for synchrotron radiation applications

Enhanced mechanical properties and corrosion resistance of Zr-based amorphous/crystalline nuclear material

Effect of target current on corrosion resistance of CrN coatings on metal bipolar plates using magnetron sputtering

PBS and XRD study on helium-charged nanocrystalline titanium film

Study on structural and surface properties of FeS₂ thin films prepared by sulfidation

Related Author

WANG Zhanshan

HUANG Qiushi

FENG Yufei

QI Runze

CHEN Jiaqi

Tao GE

Guqing GUO

Liang YANG

Related Institution

Key Laboratory of Advanced Micro-structured Materials, Ministry of Education, School of Physics Science and Engineering, Tongji University

南京航空航天大学材料科学与技术学院

College of Material Science and Technology, Nanjing University of Aeronautics and Astronautics

National Key Laboratory for Remanufacturing, the Academy of Armored Forces Engineering

Institute of Nuclear Science and Technology of Sichuan University,Key Laboratory of Radiation Physics and Technology of Education Ministry,Chen gdu 610064,China) 2

AI问答

Address：2019 Jialuo Road, Jiading, Shanghai, China Postal code：201800
Tel：021-39194977 Email：LHB@sinap.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 沪ICP备05005479号-1 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.
Total Visits：881187 Visits Today：714

⁰