Surface modification of mold steel SKD11 by high current pulsed electron beam

HAO Shengzhi1 LI Mincai1 ZHANG Xiangdong1; 2 GROSDIDIER Thierry2 DONG Chuang1 1

doi:null

您当前的位置：

首页 >

文章列表页 >

Surface modification of mold steel SKD11 by high current pulsed electron beam

更新时间：2021-03-12

- Surface modification of mold steel SKD11 by high current pulsed electron beam
- NUCLEAR TECHNIQUES Vol. 32, Issue 3, (2009)
- 作者机构：
  
  1. 大连理工大学三束材料改性重点实验室
  2. 法国梅兹大学材料织构研究与应用实验室
- 作者简介：
- 基金信息：
  
  国家高技术研究发展“863”计划项目(2006AA03Z110)资助
- DOI：
  CLC： TG142.15
- Published：01 March 2009
- 稿件说明：
移动端阅览
[1]郝胜智,李旻才,张向东,Thierry Grosdidier,董闯.SKD11模具钢的强流脉冲电子束辐照改性[J].核技术,2009,32(03):214-216.

HAO Shengzhi1 LI Mincai1 ZHANG Xiangdong1, 2 GROSDIDIER Thierry2 DONG Chuang1 1. Surface modification of mold steel SKD11 by high current pulsed electron beam[J]. Nuclear techniques, 2009, 32(3): 214-216.
[1]郝胜智,李旻才,张向东,Thierry Grosdidier,董闯.SKD11模具钢的强流脉冲电子束辐照改性[J].核技术,2009,32(03):214-216. DOI：

HAO Shengzhi1 LI Mincai1 ZHANG Xiangdong1, 2 GROSDIDIER Thierry2 DONG Chuang1 1. Surface modification of mold steel SKD11 by high current pulsed electron beam[J]. Nuclear techniques, 2009, 32(3): 214-216. DOI：

摘要

本文介绍强流脉冲电子束（HCPEB）材料表面改性原理

采用模具钢SKD11进行辐照处理实验。对处理样品表面进行形貌观察

发现熔坑面密度及粗糙度随脉冲处理次数的增加而减小。X射线衍射分析证实

多脉冲处理条件下表面改性层中碳化物发生溶解

形成高奥氏体含量的重熔组织

而过多的能量注入会使奥氏体发生再度分解。磨损性能测试表明

在低电压（19.8kV）处理情况下

耐磨损性能得到改善

脉冲次数为8次时处理样品的耐磨性达到最佳

这与表面改性层中碳化物及奥氏体的相对含量变化密切相关。

Abstract

Mechanism of surface modification technique by high current pulsed electron beam (HCPEB) was studied with SKD11 steel samples. It was found that crater-like defects would formed on the irradiated surface

the area density of craters and surface roughness decreased with the increasing number of HCPEB pulses. According to the XRD patterns

carbides in the modified surface layers dissolved after several HCPEB pulses and a high-percentage austenite microstructure is formed

but excessive energy deposition resulted in decomposition of the austenite. Treating the samples at 19.8 kV

the wear resistance of modified SKD11 steel improved and the greatest enhancement occurred at 8 pulses. Discussions were given on changes in contents of carbide and austenite in the surface layers.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Surface modification of ZK60 Mg alloy by high current pulsed electron beam

Surface morphology of Si single crystal induced by HCPEB bombardment

A study on the die steel surface modification by electron beam

A study on improvement of surface properties for V+C co-implanted stainless steel

A study on V ion implantation in embryos of sunflower

Related Author

曹辉

郝仪

高波

涂赣峰

ZHANG Wenfeng CAO Hui HAO Yi GAO Bo TU Ganfeng

梁亮

关庆丰

王雪涛

Related Institution

School of materials and metallurgy, Northeastern University

泛亚汽车技术中心有限公司

School of Environment Science and Engineering,Jiangsu University,Zhenjiang 212013,China) 2

江苏大学材料科学与工程学院

大连理工大学三束材料改性国家重点实验室

AI问答

Address：2019 Jialuo Road, Jiading, Shanghai, China Postal code：201800
Tel：021-39194977 Email：LHB@sinap.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 沪ICP备05005479号-1 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.
Total Visits：881163 Visits Today：690

⁰