Investigation of preparation technique and tribological properties of CrN piston rings coatings

CAI Zhihai1 ZHANG Ping1 ZHAO Junjun1 DU Jun1 NIU Qingyin2 1

doi:null

您当前的位置：

首页 >

文章列表页 >

Investigation of preparation technique and tribological properties of CrN piston rings coatings

更新时间：2021-03-12

- Investigation of preparation technique and tribological properties of CrN piston rings coatings
- NUCLEAR TECHNIQUES Vol. 32, Issue 6, (2009)
- 作者机构：
  
  1. 装甲兵工程学院装备再制造技术国防科技重点实验室
  2. 装甲兵工程学院训练部
- 作者简介：
- 基金信息：
  
  装备再制造技术国防科技重点实验室预研基金(9140C8502070703)资助
- DOI：
  CLC： TG174.44
- Published：01 June 2009
- 稿件说明：
移动端阅览
[1]蔡志海,张平,赵军军,杜军,牛庆银.CrN活塞环涂层的工艺制备与摩擦学性能研究[J].核技术,2009,32(06):435-438.

CAI Zhihai1 ZHANG Ping1 ZHAO Junjun1 DU Jun1 NIU Qingyin2 1. Investigation of preparation technique and tribological properties of CrN piston rings coatings[J]. Nuclear techniques, 2009, 32(6): 435-438.
[1]蔡志海,张平,赵军军,杜军,牛庆银.CrN活塞环涂层的工艺制备与摩擦学性能研究[J].核技术,2009,32(06):435-438. DOI：

CAI Zhihai1 ZHANG Ping1 ZHAO Junjun1 DU Jun1 NIU Qingyin2 1. Investigation of preparation technique and tribological properties of CrN piston rings coatings[J]. Nuclear techniques, 2009, 32(6): 435-438. DOI：

摘要

论文采用多弧离子镀技术在活塞环表面制备了CrN涂层

系统地研究了不同N2含量对CrN涂层的相结构和纳米硬度的影响规律。并采用CETR微动摩擦磨损试验机比较研究了Cr电镀层与CrN涂层的高温微动摩擦磨损性能

研究结果表明:随着N2含量的增加

薄膜由Cr2N（211）相过渡到CrN（220）相;膜层的纳米硬度随N2含量的增加而增大

并出现两个峰值;与Cr电镀层相比

CrN涂层主要以磨粒磨损为主

犁沟较窄且平滑

抗高温粘着磨损性能明显增强

而且摩擦系数较小

具有较好的摩擦匹配性能

更适合用于活塞环服役的高温磨损环境。

Abstract

By using multi-ion plating

CrN films were made on surface of piston rings to improve its tribological properties and service life.Effects of nitrogen content to prepare the film on hardness and phase structure were studied.The high-temperature tribological properties of Cr plating and CrN films were compared with CETR friction tester.The results show that nitrogen partial pressure significantly affects the mechanical properties of CrN films.With increasing N2 partial pressure

preferential growth orientation of the film changed from Cr2N(211) to CrN(220) phase

leading to two hardness peaks corresponding to the Cr2N and CrN phases

respectively.Having higher high-temperature wear resistance and lower friction coefficient than Cr plating

the CrN films are suitable for piston rings under high temperature conditions.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Tribological properties of polymer like carbon coatings on NBG-18 nuclear graphite under nitrogen environment

Effects of impact energy on morphology, structure and tribological properties of titanium nitride films deposited by energetic cluster impact

Related Author

TANG Xian

QI Wei

LIU Pengxiao

CHEN Xinchun

CHENG Jinjuan

LIU Huichuan

HAN Hai

YU Guoqing

Related Institution

School of Nuclear Science and Technology, University of South China

Jihua Laboratory

School of Mathematics and Physics, University of South China

State Key Laboratory of Tribology in Advanced Equipment, Tsinghua University

National United Engineering Laboratory for Advanced Bearing Tribology, Henan University of Science and Technology

AI问答

Address：2019 Jialuo Road, Jiading, Shanghai, China Postal code：201800
Tel：021-39194977 Email：LHB@sinap.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 沪ICP备05005479号-1 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.
Total Visits：881163 Visits Today：690

⁰