Radiation preparation and characterization of pH-sensitive hydrogel of acrylamide/β-cyclodextrin copolymer

SHAN Ting CHEN Jie YANG Liming JIE Shaowei QIAN Qiang LIN Han FAN Jinchen CAO Fangqi

doi:null

您当前的位置：

首页 >

文章列表页 >

Radiation preparation and characterization of pH-sensitive hydrogel of acrylamide/β-cyclodextrin copolymer

更新时间：2021-03-12

- Radiation preparation and characterization of pH-sensitive hydrogel of acrylamide/β-cyclodextrin copolymer
- NUCLEAR TECHNIQUES Issue 4, (2008)
- 作者机构：
  
  1. 上海大学环境与化学工程学院
  2. 上海大学环境与化学工程学院,上海,201800
- 作者简介：
- 基金信息：
  
  上海市第二期重点学科(T0105)资助
- DOI：
  CLC： O631.3
- Published：01 April 2008
- 稿件说明：
移动端阅览
[1]单廷,陈捷,杨黎明,揭少卫,钱锵,林汉,范金辰,曹芳琦.pH敏感丙烯酰胺/β-环糊精水凝胶的辐射制备及其性能研究[J].核技术,2008(04):284-287.

SHAN Ting CHEN Jie YANG Liming JIE Shaowei QIAN Qiang LIN Han FAN Jinchen CAO Fangqi. Radiation preparation and characterization of pH-sensitive hydrogel of acrylamide/β-cyclodextrin copolymer[J]. Nuclear techniques, 2008, (4): 284-287.
[1]单廷,陈捷,杨黎明,揭少卫,钱锵,林汉,范金辰,曹芳琦.pH敏感丙烯酰胺/β-环糊精水凝胶的辐射制备及其性能研究[J].核技术,2008(04):284-287. DOI：

SHAN Ting CHEN Jie YANG Liming JIE Shaowei QIAN Qiang LIN Han FAN Jinchen CAO Fangqi. Radiation preparation and characterization of pH-sensitive hydrogel of acrylamide/β-cyclodextrin copolymer[J]. Nuclear techniques, 2008, (4): 284-287. DOI：

摘要

用顺丁烯二酸酐（MAH）对β-环糊精（β-CD）进行化学改性

合成了丁烯二酸单酯化β-环糊精（MAH-β-CD）。采用电子束对MAH-β-CD和丙烯酰胺（AAm）混合水溶液辐照

制得含β-CD结构单元的水凝胶poly（AAm-co-MAH-β-CD）。研究了各组分配比、辐照剂量等对水凝胶性能的影响;测定了pH值和离子强度等因素对水凝胶溶胀率的影响。结果表明

poly（AAm-co-MAH-β-CD）水凝胶具有一定的pH敏感性和离子强度敏感性

在pH<5时

水凝胶的溶胀率较小

pH5～8时

溶胀率快速上升

最后趋于平稳;pH>5时

同一辐照剂量的水凝胶溶胀率随MAH-β-CD含量的增加明显增大

而在相同组分下水凝胶的溶胀率随剂量的增大而下降。

Abstract

A β-cyclodextrin(β-CD)based monomer(MAH-β-CD)containing vinyl and carboxyl functional groups was synthesized by reaction of β-CD with maleic anhydride(MAH).By copolymerization of the monomer with acrylamide(AAm)

a novel hydrogel

poly(AAm-co-MAH-β-CD)with pH and ionic strength sensitivities plus molecular inclusion function

was obtained by irradiating the aqueous solution mixture of AAm and MAH-β-CD with electron beam.The effect of the feed ratio of components and irradiation dose on the swelling and deswelling properties of the hydrogel was systematically studied.Swelling ratio of the hydrogel was tested under different environment of pH and ionic strength.The results indicate that the copolymer hydrogels did not show any noticeable change in swelling at lower pH(pH<5).However

they showed an abrupt increase in swelling at pH 5～8 due to the ionization of carboxyl groups.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Polyacrylamide composite hydrogel with polystyrene nanospheres prepared by one-step irradiation-induced method

Preparation of G-CNTs/PAAm hydrogel and its properties

Lithium-ion secondary battery separator prepared by radiation graft polymerization of polyacrylamide onto polypropylene membrane

Chemical stability of simulated waste forms SrZrxTi1?xO3

Low dose radiation induced adaptive response upon salt stress and vacuum stress:a possible mechanism for the effect of saddle-like dose response curve

Related Author

Wanxin WEN

Hanzhou LIU

Wenhui FAN

Wenjuan CHANG

Wenhui FAN

Xiao YU

Wanxin WEN

Siqi YAN

Related Institution

School of Radiation Medicine and Protection, Medical College of Soochow University, Jiangsu Provincial Key Laboratory of Radiation Medicine and Protection

苏州大学医学部放射医学与防护学院江苏省放射医学与防护学院重点实验室

Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Jiading Campus

Shanghai University

AI问答

Address：2019 Jialuo Road, Jiading, Shanghai, China Postal code：201800
Tel：021-39194977 Email：LHB@sinap.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 沪ICP备05005479号-1 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.
Total Visits：881163 Visits Today：690

⁰