Investigation on defects in the high temperature inorganic   scintillation single crystals of Ce:YAlO<sub>3</sub>

ZHAO Guangjun  1  LI Tao  1  HE Xiaoming  1  XU Jun  1  TIAN Yulian  2  HUANG Wanxia  2  1

doi:null

您当前的位置：

首页 >

文章列表页 >

Investigation on defects in the high temperature inorganic scintillation single crystals of Ce:YAlO₃

更新时间：2021-03-12

- Investigation on defects in the high temperature inorganic scintillation single crystals of Ce:YAlO₃
- NUCLEAR TECHNIQUES Issue 10, (2002)
- 作者机构：
  
  1. 中国科学院上海光学精密机械研究所
  2. 中国科学院高能物理研究所,上海,201800
  3. ,北京,100039
- 作者简介：
- 基金信息：
- DOI：
  CLC： O77
- Published：01 October 2002
- 稿件说明：
移动端阅览
[1]赵广军,李涛,何晓明,徐军,田玉莲,黄万霞.高温无机闪烁晶体Ce:YAlO_3的缺陷研究[J].核技术,2002(10):869-872.

ZHAO Guangjun 1 LI Tao 1 HE Xiaoming 1 XU Jun 1 TIAN Yulian 2 HUANG Wanxia 2 1. Investigation on defects in the high temperature inorganic scintillation single crystals of Ce:YAlO₃[J]. Nuclear techniques, 2002, (10): 869-872.
[1]赵广军,李涛,何晓明,徐军,田玉莲,黄万霞.高温无机闪烁晶体Ce:YAlO_3的缺陷研究[J].核技术,2002(10):869-872. DOI：

ZHAO Guangjun 1 LI Tao 1 HE Xiaoming 1 XU Jun 1 TIAN Yulian 2 HUANG Wanxia 2 1. Investigation on defects in the high temperature inorganic scintillation single crystals of Ce:YAlO₃[J]. Nuclear techniques, 2002, (10): 869-872. DOI：

摘要

采用同步辐射白光透射形貌术研究了提拉法生长的高温无机闪烁晶体Ce:YAlO3（简称Ce:YAP）中的缺陷。实验发现在Ce:YAP晶体中存在着生长条纹、包裹沉积物、核心、孪晶及位错簇等缺陷

同时对生长缺陷形成的原因进行了讨论。结果表明

离子掺杂浓度、原料的纯度以及生长工艺条件等是影响Ce:YAP晶体缺陷的主要原因

Abstract

The defects in Ce:YAlO 3 single crystals grown by Czochralski method were investigated by transmission white beam synchrotron radiation topography method. It was shown in experiments that the growth striations

inclusions precipitations

twins

core and dislocation group were the main growth defects in Ce:YAP single crystals. The mechanism of the defects formation was also discussed in the paper. The results showed that the doped concentration

purity of starting materials and growth conditions are the main causes for defects formation in Ce:YAP single crystals.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

No data

Related Author

No data

Related Institution

No data

AI问答

Address：2019 Jialuo Road, Jiading, Shanghai, China Postal code：201800
Tel：021-39194977 Email：LHB@sinap.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 沪ICP备05005479号-1 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.
Total Visits：881003 Visits Today：530

⁰

Investigation on defects in the high temperature inorganic scintillation single crystals of Ce:YAlO3

DOI：

摘要

Abstract

关键词

Keywords

references

Investigation on defects in the high temperature inorganic scintillation single crystals of Ce:YAlO₃