Synthesis of <sup>188</sup> Re-antimony sulfide nanocolloids and    their uptake by rabbit’ s lymph node

LIN Yingwu  WEI Haipeng  ZHANG Xiuli  LI Junling    YIN Duanzhi  QIU Shi  WANG Yongxian

doi:null

您当前的位置：

首页 >

文章列表页 >

Synthesis of ¹⁸⁸ Re-antimony sulfide nanocolloids and their uptake by rabbit’ s lymph node

更新时间：2021-03-12

- Synthesis of ¹⁸⁸ Re-antimony sulfide nanocolloids and their uptake by rabbit’ s lymph node
- NUCLEAR TECHNIQUES Issue 1, (2003)
- 作者机构：
  
  1. 中国科学院上海原子核研究所
  2. 中国科学院上海原子核研究所,上海,201800
- 作者简介：
- 基金信息：
- DOI：
  CLC： R817
- Published：01 January 2003
- 稿件说明：
移动端阅览
[1]林英武,魏海鹏,张秀利,李俊玲,尹端沚,邱实,汪勇先.~(188)Re-硫化锑纳米胶粒的制备及其被兔淋巴结摄取的实验研究[J].核技术,2003(01):82-85.

LIN Yingwu WEI Haipeng ZHANG Xiuli LI Junling YIN Duanzhi QIU Shi WANG Yongxian. Synthesis of ¹⁸⁸ Re-antimony sulfide nanocolloids and their uptake by rabbit’ s lymph node[J]. Nuclear techniques, 2003, (1): 82-85.
[1]林英武,魏海鹏,张秀利,李俊玲,尹端沚,邱实,汪勇先.~(188)Re-硫化锑纳米胶粒的制备及其被兔淋巴结摄取的实验研究[J].核技术,2003(01):82-85. DOI：

LIN Yingwu WEI Haipeng ZHANG Xiuli LI Junling YIN Duanzhi QIU Shi WANG Yongxian. Synthesis of ¹⁸⁸ Re-antimony sulfide nanocolloids and their uptake by rabbit’ s lymph node[J]. Nuclear techniques, 2003, (1): 82-85. DOI：

摘要

制备了两种不同粒径的硫化锑纳米胶粒

研究了1 88Re标记两种胶粒的条件以及标记物被兔窝淋巴结和腹股沟淋巴结摄取的情况。实验结果表明

两种硫化锑纳米胶粒的平均粒径分别为 10 .2nm和 4 4 .7nm。当SnCl2 ·2H2 O的浓度为 4mg mL

抗坏血酸的浓度为 6mg mL时

加入适量的1 88ReO-4淋洗液

6 0℃水浴加热 6 0min

标记率均大于 95 %

而且有较好的体外稳定性。从正常的新西兰大白兔双足趾蹼皮下分别注射两种标记物

γ探针探测的结果表明

窝淋巴结对 10 .2nm和 4 4 .7nm胶粒的摄取在注射后 1.5— 2h之间达到最大值

分别占各自注入量的17.4 %和 19.4 % ;腹股沟淋巴结对 10 .2nm和 4 4 .7nm胶粒的摄取在注射后 2h左右达到最大值

分别占各自注入量的 4 .7%和 4 .2 %。

Abstract

Two different particle sizes of antimony sulfide nanocolloids were prepared and labeled with 188 Re. Their uptake by rabbit’ s popliteal lymph node and inguinal lymph node was also studied. Results showed that the mean diameters of the two kinds of particles were 10.2nm and 44.7nm respectively. The labeling condition was optimized. When 4mg/mL SnCl 2·2H 2O

6g/L Vit C and 1mL nanocolloids were reacted in 60℃ water bath for 60min

the labeling yield were both greater than 95% and excellent in vitro stability was also observed. White New Zealand rabbits were injected subcutaneously on the dorsum of the hind foot with two kinds of 188 Re-Sb 2S 3. The uptake by popliteal lymph node and inguinal lymph node were measured quantitatively by using a gamma detecting probe. Results showed that the highest uptake of 10.2nm and 44.7nm nanocolloids by popliteal lymph node reached 17.4% and 19.4% of the total 1.5 to 2h post injection

respectively; the highest uptake by inguinal lymph node reached 4.7% and 4.2% of the total about 2h post injection

respectively.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

A new lymph node imaging agent Tc-99m-polyphase liposome

Related Author

Changying Jiang

Beiling Zhu

Yingjian Zhang

Guofen Dang

Huijuan Zhu

Related Institution

Cancer Hospital, Shanghai Medical University

AI问答

Address：2019 Jialuo Road, Jiading, Shanghai, China Postal code：201800
Tel：021-39194977 Email：LHB@sinap.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 沪ICP备05005479号-1 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.
Total Visits：881003 Visits Today：530

⁰

Synthesis of 188 Re-antimony sulfide nanocolloids and their uptake by rabbit’ s lymph node

DOI：

摘要

Abstract

关键词

Keywords

references

Synthesis of ¹⁸⁸ Re-antimony sulfide nanocolloids and their uptake by rabbit’ s lymph node