Study of TiCxNy films formed by ion beam assisted depositionon 9Cr18 steel

doi:null

您当前的位置：

首页 >

文章列表页 >

Study of TiCxNy films formed by ion beam assisted depositionon 9Cr18 steel

更新时间：2021-03-12

- Study of TiCxNy films formed by ion beam assisted depositionon 9Cr18 steel
- NUCLEAR TECHNIQUES Issue 1, (1999)
- 作者机构：
  
  1. 四川联合大学原子核科学技术研究所
  2. 辐射物理与技术国家教委开放实验室!成都６１００６４
  3. 四
- 作者简介：
- 基金信息：
- DOI：
  CLC： TG174.444
- Published：01 January 1999
- 稿件说明：
移动端阅览
[1]王培录,孙官清,刘仲阳,郑思孝,廖小东.9Cr18钢上离子束辅助沉积TiC_xN_y膜的研究[J].核技术,1999(01):6-10.

Study of TiCxNy films formed by ion beam assisted depositionon 9Cr18 steel[J]. Nuclear techniques, 1999, (1): 6-10.
[1]王培录,孙官清,刘仲阳,郑思孝,廖小东.9Cr18钢上离子束辅助沉积TiC_xN_y膜的研究[J].核技术,1999(01):6-10. DOI：

Study of TiCxNy films formed by ion beam assisted depositionon 9Cr18 steel[J]. Nuclear techniques, 1999, (1): 6-10. DOI：

摘要

用离子束辅助沉积技术在９Ｃｒ１８钢基体上形成了ＴｉＣｘＮｙ膜。ＴＥＭ观察膜呈多晶结构，具有（１１１）、（２００）和（２２０）择优取向。ＡＥＳ和ＸＰＳ分析进一步证实，ＴｉＣｘＮｙ膜呈含氧配置。膜的硬度与Ｎ含量有关，Ｎ的含量过高时硬度下降。在本实验条件下以离子注量为３ｘ１０１7／ｃｍ２时硬度最高，干摩擦表明膜的抗氧化性能优良，它的存在能有效抑制基体在摩擦过程中氧化皮的形成，显著改善基体的磨损特性，并能使基体由粘着磨损向磨粒磨损转化．

Abstract

The TiCxNy films were formed on 9Cr18 steel matrix using the ion beam assisteddeposition. The TEM analysis revealed the films with a polycrystalline structure with(111)

(200) and (220) preferred orientation. The fact that TiCxNy films contain oxygencoordination was further confirmed by AES and XPS. Microhardness of the films wasfound dependent on its N content

and it was decreased for an excessively high Ncontent. An assisted dose of 3 X 1017/cm2 is optimum in this experiment. A dry frictiontest indicated that oxidation resistance of the films is excellent

and oxidation of thesteel matrix in the friction process can be obviously inhibited. Both the abrasive andadhesive wears of matrix are improved

and a trend of transformation from adhesiveinto abrasive wear appears for the steel matrix.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Characteristics of Mos_x films deposited by ion beam assistance

Anti wear property of GCr15 steel deposited with Ta film and implanted with C ions

Property of multilayer TiCN films formed by ion-beam-assisted-deposition

Experimental study of nano-composite superhard TiN/Si₃₄ films prepared by ion beam assisted deposition

Low energy Ar~+ beam assisted deposition of Ag(111) films

Related Author

杨兴富

姜景云

刘仲阳

王培禄

孙明仁

马欣新

唐光泽

LI Zhongwen TANG Guangze MA Xinxin SUN Mingren

Related Institution

Institute of Nuclear Science and Technology, Sichuan University

School of Materials Science and Engineering,Harbin Institute of Technology

北京航空航天大学机械自动化学院

Beijing Research Institute of Automation for Machinery Industry

National Key Laboratory for Remanufacturing, Academy of Armored Force Engineering

AI问答

Address：2019 Jialuo Road, Jiading, Shanghai, China Postal code：201800
Tel：021-39194977 Email：LHB@sinap.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 沪ICP备05005479号-1 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.
Total Visits：880840 Visits Today：367

⁰