A positron annihilation study of heat treatment effect on corrosion behaviour of a Ni-17—19 at% P amorphous alloy

Jingcheng Wang; Liqun Feng

您当前的位置：

首页 >

文章列表页 >

A positron annihilation study of heat treatment effect on corrosion behaviour of a Ni-17—19 at% P amorphous alloy

更新时间：2022-09-13

- A positron annihilation study of heat treatment effect on corrosion behaviour of a Ni-17—19 at% P amorphous alloy
- Nuclear Techniques Vol. 10, Issue 10, (1987)
- 作者机构：
  
  上海钢铁研究所
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：01 September 1986，
  
  Published：1987-10
- 稿件说明：
移动端阅览
Jingcheng Wang, Liqun Feng. A positron annihilation study of heat treatment effect on corrosion behaviour of a Ni-17—19 at% P amorphous alloy[J]. Nuclear techniques, 1987, 10(10): 11-12,57.
DOI：

Jingcheng Wang, Liqun Feng. A positron annihilation study of heat treatment effect on corrosion behaviour of a Ni-17—19 at% P amorphous alloy[J]. Nuclear techniques, 1987, 10(10): 11-12,57. DOI：

摘要

测量了Ni-17—19at%P|非晶态合金经不同温度处理后的正电子湮没多普勒展宽能谱线形

参数。分析表明，晶间腐蚀和偏离化学成分配比是导致该合金晶化后耐腐蚀性能变坏的两个可能原因。

Abstract

S-lineshape parameters of Doppler-broadening of positron annihilation were measured for a Ni-17—19 at% P amorphous alloy treated at different temperature. Results suggest that grain boundary corrosion and deviation from stoichiometric composition may be the possible factors resulting in low corrosion resistance of the alloy.

关键词

Keywords

references

冯力群等，腐蚀与防护， 1 ， 17 （ 1986 ）.

H. S. Chen and S. Y. Chuang , Phys. Stat. Sol （ a ） ., 25 , 581 （ 1974 ）.

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Application of positron annihilation to study the effect of calcium oxide addition on the sintering process of alumina nanoceramics

Positron annihilation study on defect repair of pure iron and RPV steel under electropulsing treatment

Effect of corrosion on boiling heat transfer characteristics of metal specimens with micro-structure surface

Distribution of pH values in a model simulating the secondary side of a steam generator

Study on the microstructure and defects of Al₂O₃/ZrO₂ nano-composites by positron lifetime spectroscopy

Related Author

YANG Xuanye

ZHAO Wenzheng

ZHANG Simin

WEN Haiyi

WU Yichu

WEN Haiyi

YANG Xuanye

ZHAO Wenzeng

Related Institution

School of Physics and Technology, Hubei Key Laboratory of Nuclear Solid State Physics, Wuhan University

Suzhou Nuclear Power Research Institute

School of Nuclear Science and Engineering, Shanghai Jiao Tong University

Science and Technology on Reactor System Design Technology Laboratory, Nuclear Power Institute of China

College of Chemistry, Fuzhou University

AI问答

Address：2019 Jialuo Road, Jiading, Shanghai, China Postal code：201800
Tel：021-39194977 Email：LHB@sinap.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 沪ICP备05005479号-1 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.
Total Visits：880565 Visits Today：92

⁰