首页 >

文章列表页 >

Cu-Al-Zn-Mn-Ni形状记忆合金的正电子湮没研究

更新时间：2022-09-13

- Cu-Al-Zn-Mn-Ni形状记忆合金的正电子湮没研究
- Nuclear Techniques Vol. 08, Issue 8, (1985)
- 作者机构：
  
  1.中国科学院高能物理研究所
  2.哈尔滨工业大学
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：1985-11
- 稿件说明：
移动端阅览
[J]. Nuclear techniques, 1985, 08(8): 22-23.
DOI：

[J]. Nuclear techniques, 1985, 08(8): 22-23. DOI：

摘要

Cu-Al-Zn-Mn-Ni为形状记忆合金。本文采用正电子湮没寿命和多普勒展宽参数的测量对该合金在不同工艺处理后的内部结构作进一步研究。熔炼两种成份合金，其化学成份和相变点如下表所示，试样均在865℃加热20min，然后分别淬入200—-196℃不同温度的冷却介质中，及热轧后水冷、热轧后冷轧和热轧后退火等14种不同的工艺处理。

Abstract

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Application of positron annihilation techniques in non-destructive testing

A study of damages in GaAs induced by 5.0MeV and 9.5MeV fastneutron irradiation using positron annihilation technique

X-ray diffraction and positron annihilation study on crystalline process of Fe_73.5Cu₁Nb₃Si_13.5B₉ amorphous alloy

Investigation of interaction between hydrogen and defects in corrosion fatigue fracture process by positron annihilation

A study of the influence of γ-irradiation on brittleness of amorphous alloy Fe₇₈Si₉B₁₃

Related Author

ZENG Hui

CHEN Zhiqiang

JIANG Jing

XUE Xudong

LIANG Jianping

LIU Xiangbing

WANG Rongshan

WU Yichu

Related Institution

School of Physics and Technology, Hubei Key Laboratory of Nuclear Solid State Physics, Wuhan University

Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Jiading Campus

Center of Plant Life Management, Suzhou Nuclear Power Research Institute

China Institute of Atomic Energy

北京有色金属研究总院

AI问答

Address：2019 Jialuo Road, Jiading, Shanghai, China Postal code：201800
Tel：021-39194977 Email：LHB@sinap.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 沪ICP备05005479号-1 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.
Total Visits：880523 Visits Today：50

⁰