Changes of adhesion of Au and Ag films on muscovite mica induced by MeV ion-beam bombardment

Huazhong Yang; Zhengmin Liu; Kunshan Yang; Yuanxun Qiu

您当前的位置：

首页 >

文章列表页 >

Changes of adhesion of Au and Ag films on muscovite mica induced by MeV ion-beam bombardment

更新时间：2022-08-16

- Changes of adhesion of Au and Ag films on muscovite mica induced by MeV ion-beam bombardment
- Nuclear Techniques Vol. 13, Issue 8, (1990)
- 作者机构：
  
  1.兰州大学
  2.复旦大学
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：01 February 1989，
  
  Published：1990-08
- 稿件说明：
移动端阅览
Huazhong Yang, Zhengmin Liu, Kunshan Yang, et al. Changes of adhesion of Au and Ag films on muscovite mica induced by MeV ion-beam bombardment[J]. Nuclear techniques, 1990, 13(8): 449-452.
DOI：

Huazhong Yang, Zhengmin Liu, Kunshan Yang, et al. Changes of adhesion of Au and Ag films on muscovite mica induced by MeV ion-beam bombardment[J]. Nuclear techniques, 1990, 13(8): 449-452. DOI：

摘要

本文叙述了用能量为1—4MeV的Cl离子轰击有Au和Ag薄膜的天然白云母，使金属膜与白云母界面之间的附着力发生了变化。用胶带法测试了不同离子能量下的增强附着剂量阈

。入射Cl离子的剂量在增强附着剂量阈以上时，界面之间有增强附着力的存在，而在剂量阈以下，发现了附着力的减弱现象。金和白云母系统只测到了一个剂量阈；而银和白云母系统测出了两个剂量阈。用王水腐蚀白云母上的金属膜时，腐蚀时间随照射剂量的增加而延长。

Abstract

Cl ionbeam induced changes of adhesion of thin Au and Ag films on muscovite mica substrates have been studied for beam energies ranging from 1.02 to 4.02 MeV and for a wide range of doses. Threshold doses (

) of enhanced adhesion for different energies have been measured by the Scotch Tape Test. It is found that after ion bombardment with a dose less than

the adhesion of thin metal im on mica substrate becomes weaker. The lower the Cl ion irradiation dose the more obvious this phenomenon. An acid (aquaregia) corrosion test indicates that the corrosion resisting time of irradiated metal films is prolonged with inorease of the Cl ion doses.

关键词

Keywords

references

裘元勋，核技术，（ 1986 ）， 7 ： 1 .

C. R. Wie et al ., Nucl. Instr. Meth. , B9 （ 1985 ）, 20 .

J. E. Griffith et al ., Nucl. Instr. Meth. , 198 （ 1982 ）, 607 .

T. A. Tombrello , Int. J. Mass. Spectrom. Ion Phys. , 53 （ 1983 ）, 307 .

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Slow positron beam study on defects induced by Xe ions irridiation in matrix graphite of fuel elements

Thermodynamic study on phase stability of plutonium under irradiation

Investigation of helium irradiation induced hardening in nickel-based alloy

Radiation effects on physicochemical characteristics of pork

The biological effect of Pistacia chinensis Bunge by ⁶⁰Co γ-ray irradiation

Related Author

XU Hongxia

LIN Jun

ZHU Zhiyong

LIU Jiandang

GU Bingchuan

YE Bangjiao

Yong LU

Qiaoqiao TANG

Related Institution

State Key Laboratory of Particle Detection and Electronics, University of Science and Technology of China

Shanghai Institute of Applied Physics, Chinese Academy of Sciences

College of Materials, Xiamen University

University of Chinese Academy of Sciences

Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Jiading Campus

AI问答

Address：2019 Jialuo Road, Jiading, Shanghai, China Postal code：201800
Tel：021-39194977 Email：LHB@sinap.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 沪ICP备05005479号-1 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.
Total Visits：880718 Visits Today：245

⁰