Silver-brass alloy mixing layer formed by ion beam mixing and its friction property

Peilu Wang; Xigang Lin; Jingyun Jiang; Yuanru Chen

您当前的位置：

首页 >

文章列表页 >

Silver-brass alloy mixing layer formed by ion beam mixing and its friction property

更新时间：2022-08-16

- Silver-brass alloy mixing layer formed by ion beam mixing and its friction property
- Nuclear Techniques Vol. 09, Issue 8, (1986)
- 作者机构：
  
  四川大学原子核科学技术研究所
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：1986-08
- 稿件说明：
移动端阅览
Peilu Wang, Xigang Lin, Jingyun Jiang, et al. Silver-brass alloy mixing layer formed by ion beam mixing and its friction property[J]. Nuclear techniques, 1986, 09(8): 53-57,F3.
DOI：

Peilu Wang, Xigang Lin, Jingyun Jiang, et al. Silver-brass alloy mixing layer formed by ion beam mixing and its friction property[J]. Nuclear techniques, 1986, 09(8): 53-57,F3. DOI：

摘要

黄铜是工业上应用十分广泛的一种合金材料，若能改善其表面的摩擦性能，又保持基体原有的强度，将是具有实际意义的。为此，我们用离子束混合技术将银引入黄铜基体，在表面生成了润滑性能良好的银-黄铜合金混层，并对其摩擦性能、强度及与基体的结合力作了对比试验，然后用AES、SIMS、SEM以及光学显微镜对其混合状态和表面形貌作了分析和观察。

Abstract

An experimental process in formming silver-brass alloy mixing layer by ion beam mixing in brass matrix was described. Both the bondstrength and the friction-coefficient of the mixing layer were measured. The intermixing of silver atoms with brass matrix was confirmed by means of AES and SIMS profiling analysis.

关键词

Keywords

references

J. M. Poate , Appl. Phys. Lett. , 30 , 365 （ 1977 ）.

Z. L. Liau et al . , J. Vac. Sci. Technol. , 15 , 1629 （ 1978 ）.

B. Y. Tsaur et al . , Appl. Phys. Lett. , 36 , 823 （ 1980 ）.

H. H. Andersen and H. L. Bay , Sputtering-yield measurements , Institute of Physics, University of Aarhus-Denmark , 1980 .

U. Littmark et al . , Nucl. Instr. Meth. , 168 , 329 （ 1980 ）.

B. Y. Tsaur et al . , ibid , 182/183 , 67 （ 1981 ）.

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Anodic polarization of hard aluminium: the influence of ion beam twice mixing on corrosion behaviour

The corrosion resistance of No.45 steel mixed with several different elements

Synchrotron radiation photoemission spectroscopy study on the phenomenon of alloying during stanene growth

Study of intense pulsed ion beam mixing with RBS

Micrscopic study of H~+ irradiation effect on the tungsten film deposited on stainless steel

Related Author

Peilu Wang

Zhongyang Liu

Jingyun Jiang

Wenshu Han

Zhongyang Liu

Yirong Wang

Jin Chen

Gholam Turghunjan

Related Institution

Institute of Nuclear Science and Technology, Sichuan Vniversity

Chengdu Aeroengine Company

University of Chinese Academy of Sciences

Institute of High Energy Physics, Chinese Academy of Sciences

Beijing Huaneng Xinrui Control Technology Co., Ltd.

AI问答

Address：2019 Jialuo Road, Jiading, Shanghai, China Postal code：201800
Tel：021-39194977 Email：LHB@sinap.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 沪ICP备05005479号-1 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.
Total Visits：880565 Visits Today：92

⁰